Home PLA Wood

PLA Wood

Selected:
Size: 1.75MM | Weight: 1 KG | Color: White Oak
Sale price AED 140.00
Size: 1.75MM
Weight: 1 KG
Color: White Oak
SKU: A16-W0-1.75-1000-SPL
Product Features
  • Feels Like Real Wood
  • Matte Finish, Fine Texture
  • Integrates Perfectly with Other PLA
  • Comes with Basic Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm
Cautions for Use
  • All AMS Series Compatible
  • 0.2 mm Nozzle Not Compatible
  • Dry Out Before Use
Add to Wishlist Add to Compare

Notify me when available

Register to receive a notification when this item comes back in stock.

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby

Feels Like Real Wood

Bambu PLA Wood offers a smooth yet slightly grainy texture, with the feel of real wood. With natural wood-like colors and a subtle scent, your models will embody the essence of genuine wood. Perfect for projects that demand a true-to-life wood aesthetic, Bambu PLA Wood blends beauty and authenticity for a natural finish.

Matte Finish, Fine Texture

The matte finish of Bambu PLA Wood effectively conceals layer lines, delivering smoother, more refined prints. Its seamless surface enhances the overall aesthetic, giving your creations an authentic, real-wood appearance.

Enhance Your PLA Models with Wood Accents

Bambu PLA Wood integrates seamlessly with other Bambu PLA filaments like PLA Basic and PLA Matte, allowing you to combine natural wood textures with vibrant colors. Mix and match textures in a single print to unlock endless creative possibilities and bring your designs to life

Bambu Lab PLA Wood Technical Specifications

Nozzle Temperature 190 - 240 °C
Bed Temperature (with Glue) 35 - 45 °C
Printing Speed < 250 mm/s
Container Humidity < 20% RH (Sealed, with Desiccant)
Drying Method Blast Drying Oven
Drying Temperature 55 °C
Drying Time 8 hours
Density 1.21 g/cm³
Vicat Softening Temperature 64 °C
Heat Deflection Temperature 57 °C
Melting Temperature 156 °C
Melt Index 29.4 ± 1.7 g/10 min
Tensile Strength 26 ± 5 MPa
Breaking Elongation Rate 15.3 ± 3.1 %
Bending Modulus 2780 ± 120 MPa
Bending Strength 55 ± 4 MPa
Impact Strength 15.7 ± 3.7 kJ/m²