Home Bambu Lab PAHT-CF 3D Printing Filament

Bambu Lab PAHT-CF 3D Printing Filament

SKU: N04-K0-1.75-1000-SPL
Bambu Lab

Selling fast! 52 people have this in their carts.

Sale price AED 439.00
Size: 1.75MM
Weight: 1 KG
Color: Black

Product Features

  • Low Moisture Absorption
  • Exceptional Mechanical Properties & Layer Adhesion
  • High Tensile Strength
  • Comes with High Temperature Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm


Cautions for Use

  • 0.6 mm Nozzle Recommended
  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • Dry before Use
  • AMS Compatible
  • AMS lite NOT Compatible
  • Enclosure Printer Required
Add to Wishlist Add to Compare
Order in the next to get it between and

Estimate delivery times: 1-2 days

Return within 2 days of purchase.

Guarantee Safe Checkout

Bambu Lab PAHT-CF 3D Printing Filament

Bambu Lab PAHT-CF 3D Printing Filament

Low water absorption

With a 50% lower water absorption rate compared to normal PA-CF, Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.

Exceptional Z-bonding

Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF, bringing it the ability to withstand high levels of impact or stress without breaking or deforming.

High tensile strength

Bambu PAHT-CF is designed to meet the demands of various industrial and engineering applications where high strength and durability are required.

Technical Specifications

Drying Settings (Blast Drying Oven) 80 °C, 8 - 12 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 260 - 290 °C
Bed Temperature (with Glue) 80 - 100 °C
Printing Speed < 100 mm/s
Density 1.06 g/cm³
Vicat Softening Temperature 220 °C
Heat Deflection Temperature 194 °C
Melting Temperature 225 °C
Melt Index 14.4 ± 2.0 g/10 min
Tensile Strength 92 ± 7 MPa
Breaking Elongation Rate 8.4 ± 1.8 %
Bending Modulus 4230 ± 210 MPa
Bending Strength 125 ± 7 MPa
Impact Strength 57.5 ± 3.4 kJ/m²