Home PLA Aero

PLA Aero

Selected:
Size: 1.75MM | Weight: 1 KG | Color: White
Bambu Lab

Selling fast! 11 people have this in their carts.

Sale price AED 220.00
Size: 1.75MM
Weight: 1 KG
Color: White
SKU: A11-W0-1.75-1000-SPL

Product Features

  • Specialized for 3D RC Planes Printing
  • Low Density and Light Weight
  • Tough with Good Impact Resistance
  • Matte Finish For Easy Coloring
  • Comes with Basic Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm


Cautions for Use

  • Recommended to dry out before use
  • AMS & AMS lite Compatible
Add to Wishlist Add to Compare
Order in the next to get it between and

Ask a question
Share

Estimate delivery times: 1-2 days

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
PLA Aero

PLA Aero

Controllable Model Density

Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA. It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys.
Carbon fiber texture & Minimized layer lines
The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look.
Display of Prints
Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements.

Tough with Good Impact Resistance

RFID for Intelligent Printing

Technical Specifications

Drying Settings (Blast Drying Oven) 55 °C，8 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 220 - 260 °C
Bed Temperature (with Glue) 35 - 45 °C
Printing Speed < 180 mm/s
Density 1.21 g/cm³
Vicat Softening Temperature 54 °C
Heat Deflection Temperature 53 °C
Melting Temperature 153 °C
Melt Index 7.7 ± 0.6 g/10 min
Tensile Strength 24 ± 2 MPa
Breaking Elongation Rate 2.6 ± 0.7 %
Bending Modulus 1690 ± 120 MPa
Bending Strength 45 ± 4 MPa
Impact Strength 28.8 ± 1.3 kJ/m²