Home Bambu Lab TPU 95A HF 3D Printer Filament

Bambu Lab TPU 95A HF 3D Printer Filament

SKU: U00-W0-1.75-1000-SPL
Bambu Lab

Selling fast! 30 people have this in their carts.

Sale price AED 186.00
Size: 1.75MM
Weight: 1 KG
Color: White

Product Features

  • High-speed printing TPU
  • Soft, Flexible & Tough
  • Outstanding Impact Resistance and Flexibility
  • Includes High Temperature Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm


Cautions for Use

  • Dry out before use
  • AMS & AMS lite NOT Compatible
Add to Wishlist Add to Compare
Order in the next to get it between and

Compare color

Bambu Lab TPU 95A HF 3D Printer Filament
White
Bambu Lab TPU 95A HF 3D Printer Filament
Black
Bambu Lab TPU 95A HF 3D Printer Filament
Blue
Bambu Lab TPU 95A HF 3D Printer Filament
Grey
Bambu Lab TPU 95A HF 3D Printer Filament
Red
Bambu Lab TPU 95A HF 3D Printer Filament
Yellow

Ask a question
Share

Estimate delivery times: 1-2 days

Return within 2 days of purchase.

Guarantee Safe Checkout

Bambu Lab TPU 95A HF 3D Printer Filament

Bambu Lab TPU 95A HF 3D Printer Filament

High Speed Printing

Elevate your TPU printing efficiency to the next level with Bambu TPU 95A HF, featuring a print speed that's 3 times faster than standard TPU 95A.

Soft and Flexible

Bambu TPU HF is an exceptionally soft and flexible filament with extraordinary impact resistance, enabling you to print parts that need withstand impact, collision, and falling.

Widely Used Application

PU 95A HF maintains exceptional interlayer adhesion, impact resistance, flexibility, and cold-temperature resilience, just like traditional TPU filaments. Experience faster TPU printing without any compromises!

Technical Specifications

Drying Settings (Blast Drying Oven) 70 °C，8 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 220 - 240 °C
Bed Temperature (with Glue) 30 - 35 °C
Printing Speed < 200 mm/s
Density 1.22 g/cm³
Vicat Softening Temperature N / A
Heat Deflection Temperature N / A
Melting Temperature 183 °C
Melt Index 36.5 ± 2.6 g/10 min
Tensile Strength 27.3 ± 0.8 MPa
Breaking Elongation Rate > 650%
Bending Modulus N / A
Bending Strength N / A
Impact Strength N / A