Home PLA-CF

PLA-CF

Selected:
Size: 1.75MM | Weight: 1 KG | Color: Black
eSUN

Selling fast! 7 people have this in their carts.

Sale price AED 90.00
Size: 1.75MM
Weight: 1 KG
Color: Black
SKU: PLA-CF175B1Y1

Features

  • High Toughness & High Strength
  • Low Shrinkage & Low Water Absorption
  • Shine-free Matte Printed Surface
  • High Speed Printing & Fast Cooling
  • High Compatibility & Wide Application
Add to Wishlist Add to Compare
Order in the next to get it between and

Compare color

PLA-CF
Black
PLA-CF
Red
PLA-CF
Green
PLA-CF
Purple
PLA-CF
Brown

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
PLA-CF

PLA-CF
Improved based on ordinary PLA, eSUN PLA CF carbon fiber PLA filament adds organic infiltrated chopped carbon fiber imported from Germany, which makes it present a better carbon fiber performance. High flexural modulus. Less wear on nozzles compared to PA CF.
Compared to PA CF, eSUN PLA CF has lower shrinkage and lower water absorption. Also, because it is based on PLA, it has the characteristic of PLA and doesn't need to print in enclosed chamber.No bubbles, less stringing, high successful printing rate.Stable dimensional tolerence.Good winding, does not overlap or tangle.
With chopped carbon fiber added, eSUN PLA CF presents an excellent shine-free matte printed surface and distinctive carbon fiber frosted texture. Also, the printed model doesn't have obvious layer lines compared to normal PLA.
eSUN PLA CF can maintain the printing quality and retain the integrity of the complete fine structures without layer lines and deformation while printing in high speed.Fast cooling.Printing Speed 50-300mm/s.
Whether used as structural components or for aesthetic purposes, PLA CF effortlessly excels, thanks to its outstanding attributes.Widely used in machinery, chemical industry, fixture, robots, unmanned aerial vehicle, automobiles, textile, aerospace and other field.

eSUN PLA-CF Technical Specifications

Extruder Temperature 190-230°C
Bed Temperature 45-60°C
Fan Speed 100%
Printing Speed <200mm/s
Heated Bed Need
Printing Suggestions Use hardened steel nozzle
Need to Dry √
Density 1.21 g/cm³
Melt Flow Index 5.37 (190°C/2.16kg)
Heat Distortion Temp (0.45MPa) 53°C
Tensile Strength (XY) 59.64 MPa
Tensile Strength (Z) 31.78 MPa
Elongation at Break (XY) 5.26%
Elongation at Break (Z) 2.91%
Flexural Strength (XY) 96.1 MPa
Flexural Strength (Z) 53.1 MPa
Flexural Modulus (XY) 5431.38 MPa
Flexural Modulus (Z) 3184.76 MPa
IZOD Impact Strength (XY) 4.03 kJ/m²
IZOD Impact Strength (Z) 2.16 kJ/m²