Home Fiberon ASA-CF08

Fiberon ASA-CF08

Selected:
Size: 1.75MM | Weight: 0.5 KG | Color: Black
Fiberon

Selling fast! 2 people have this in their carts.

Sale price AED 140.00
Size: 1.75MM
Weight: 0.5 KG
Color: Black
SKU: FF02001

Product Features

  • Engineered for Performance
  • Excellent Mechanical Strength
  • High Heat Resistance
  • Excellent Surface Finish
  • Easy To Print
  • Moisture & Tangle Free
Add to Wishlist Add to Compare
Order in the next to get it between and

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
Fiberon ASA-CF08

Fiberon ASA-CF08
Engineered for Performance
Fiberon™ ASA-CF08 combines the UV and weather resistance of ASA with 8% carbon fiber by weight, delivering high rigidity, reduced warping, and a professional matte finish.
Excellent Mechanical Strength
With a bending strength of 69.1 MPa (XY) and tensile strength of 43.5 MPa (XY), ASA-CF08 offers the reliability needed for load-bearing and precision parts.

High Heat Resistance
ASA-CF08 has an HDT of up to 103 °C @0.45 MPa, making it perfect for enclosures, fixtures, and components exposed to direct sunlight or extreme heat without deformation.
Excellent Surface Finish
With 6 color options available and a high quality matte finish that hides layer lines, ASA-CF08 is ideal for applications where aesthetics matter as much as function.

Easy To Print
ASA-CF08 supports high-speed printing up to 350 mm/s, is less prone to warping and requires minimal chamber heating, making it a versatile choice for both professionals and hobbyists.
Moisture & Tangle Free
Each spool is vacuum-sealed and tangle-free so your prints stay smooth and your workflow uninterrupted.

Fiberon ASA CF-08 Technical Specifications

Nozzle Temperature 260 - 280 °C
Build Plate Temperature 90 - 100 °C
Chamber Temperature Room temp.
Cooling Fan OFF
Printing Speed Up to 350 mm/s
Drying Temperature and Time 90 °C/6H
Annealing Temperature and Time N/A
Density 1.09 g/cm³ at 23°C
Melt Index 13.9 g/10min (240°C, 5 kg)
Flame Retardancy HB (UL 94, 1.5mm)
Surface Resistivity (Ω) 0L, >10¹² Ω
Glass Transition Temperature 106.6 °C
Melting Temperature N/A
Crystallization Temperature N/A
Decomposition Temperature 328.4 °C
Vicat Softening Temperature 110.8 °C
Heat Deflection Temperature (1.8MPa) 97.3 °C
Heat Deflection Temperature (0.45MPa) 103.0 °C
Young's Modulus (X-Y) 3611.7 ± 181.1 MPa
Young's Modulus (Z) 1903.8 ± 71.0 MPa
Tensile Strength (X-Y) 43.5 ± 0.7 MPa
Tensile Strength (Z) 25.0 ± 0.4 MPa
Elongation at Break (X-Y) 1.8 ± 0.1%
Elongation at Break (Z) 2.7 ± 0.2%
Bending Modulus (X-Y) 3265.0 ± 56.5 MPa
Bending Modulus (Z) 1743.4 ± 59.9 MPa
Bending Strength (X-Y) 69.1 ± 1.62 MPa
Bending Strength (Z) 46.5 ± 0.8 MPa
Charpy Impact Strength (X-Y) Notched 5.5 ± 0.14 kJ/m²
Charpy Impact Strength (X-Y) Un-notched 11.0 ± 0.5 kJ/m²
Charpy Impact Strength (Z) Un-notched 11.9 ± 0.9 kJ/m²