Home Fiberon PA6-GF25

Fiberon PA6-GF25

Selected:
Size: 1.75MM | Weight: 0.5 KG
Fiberon

Selling fast! 16 people have this in their carts.

Sale price AED 175.00
Size: 1.75MM
Weight: 0.5 KG
SKU: FG02001

High-Performance Composite: Glass fiber-reinforced Nylon 6 with excellent strength, durability, and heat resistance.

Excellent Printability: Maintains strong layer adhesion and print quality across mainstream and entry-level printers.

Tangle-Free & Moisture-Resistant: Neatly wound and sealed with desiccant in a resealable bag for clean, dry storage.

Eco-Friendly Packaging: Durable recycled cardboard spool with reinforced edges for long-term protection.

Add to Wishlist Add to Compare
Order in the next to get it between and

Ask a question
Share

Estimate delivery times: 1-2 days

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
Fiberon PA6-GF25

Fiberon PA6-GF25

Transform your professional 3D printing applications with Fiberon PA6-GF25, an advanced glass fiber reinforced PA6 (Nylon 6) filament engineered to deliver superior thermal and mechanical properties for demanding industrial applications. The strategic glass fiber reinforcement significantly enhances mechanical strength and stiffness while maintaining lightweight characteristics, making it ideal for parts requiring exceptional durability under high stress and mechanical loads. With excellent heat resistance that maintains structural integrity at elevated temperatures and outstanding thermal stability for consistent performance across fluctuating temperature environments, this material excels in automotive components, industrial machinery parts, and high-performance engineering applications.

Experience revolutionary printing reliability with Fiberon PA6-GF25's warp-free properties that enable smooth, precise printing even on large parts and complex geometries without dimensional distortion. The advanced formulation ensures minimal shrinkage during cooling, maintaining exact dimensions and form integrity throughout the printing process. This high-performance material delivers exceptional print quality with smooth surface finishes, consistent layering, and remarkable dimensional accuracy, even at high printing speeds. The superior layer adhesion and excellent mechanical properties, including high tensile strength and impact resistance, ensure parts can withstand heavy loads and mechanical stresses while maintaining professional-grade aesthetics.

Optimized Production Efficiency: Tailored for high-speed printing capabilities that reduce completion times without compromising part quality, delivering speed and efficiency across professional and entry-level 3D printer platforms
Universal Printer Access: Enhanced compatibility with wide range of 3D printers, including entry-level models, enables industrial-grade results without requiring specialized or expensive equipment investments
Versatile Industry Applications: Perfect for automotive engine parts and interior components, aerospace lightweight high-stress parts, industrial tooling fixtures and jigs, consumer goods requiring durability, and functional prototyping for testing applications across automotive, aerospace, industrial machinery, and consumer product sectors

Technical Specifications

Nozzle Temperature 280 - 300°C
Build Plate Temperature 40 - 50°C
Printing Speed Up to 300 mm/s
Printing and Keeping Container's Humidity 70% RH, 23°C
Drying Settings (Blast Drying Oven) 100°C / 10H
Density 1.20 g/cm³ at 23°C
Vicat Softening Temperature N / A
Heat Deflection Temperature 191°C
Melting Temperature 214.5°C
Melt Index 15.9 g/10min
Tensile Strength 80.1 ± 1.8 MPa
Breaking Elongation Rate 2.4 ± 0.2%
Bending Strength 133.8 ± 4.7 MPa
Bending Modulus 4314.22 ± 120.6 MPa
Impact Strength 27.4 ± 0.5 kJ/m²