Home Fiberon™ PET-GF15

Fiberon™ PET-GF15

Selected:
Size: 1.75MM | Weight: 1 KG | Color: Black
Fiberon

Selling fast! 4 people have this in their carts.

Sale price AED 135.00
Size: 1.75MM
Weight: 1 KG
Color: Black
SKU: FL02001
Features:
  • High-Strength, Heat-Resistant Engineering Filament
  • Industrial-Level Performance, Everyday Usability
  • Excellent Surface Finish & AMS Compatible
  • Dimensional Stability & Low Warping
  • Designed for Professionals & Makers Alike
Printing Requirements:
  • PET-GF filament adheres strongly to textured PEI plates—allow plate to cool before removal or use a release agent to prevent damage.
  • Hardened nozzle
Add to Wishlist Add to Compare
Order in the next to get it between and

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
Fiberon™ PET-GF15

Fiberon™ PET-GF15

Fiberon™ PET-GF15 – Glass-Fiber-Reinforced PET Filament

Bridge the gap between everyday usability and industrial performance.
High-Strength, Heat-Resistant Engineering Filament
Fiberon™ PET-GF15 combines PET with 15% glass fiber reinforcement to deliver exceptional stiffness, dimensional stability, and thermal resistance. It’s engineered for users who need the toughness of an engineering-grade filament without sacrificing printability.
Industrial-Level Performance, Everyday Usability
With a bending strength of 104 MPa and HDT up to 133 °C (0.45MPa, after annealing), PET-GF15 withstands high stress and high-temperature environments where other materials would deform. It prints easily on most modern FDM printers, even at speeds up to 250 mm/s.
Excellent Surface Finish & AMS Compatible
Achieve smooth, professional-grade prints with a refined texture that minimizes visible layer lines. Available in six vibrant colors, Fiberon™ PET-GF15 works seamlessly with most multi-material systems, perfect for multi-color and multi-material projects.
Dimensional Stability & Low Warping
PET-GF15 maintains consistent accuracy and minimal warping, even on large projects. After annealing, dimensional change stays below 0.5 %, ensuring tight tolerances for functional parts that demand reliability and precision.
Designed for Professionals & Makers Alike
Ideal for automotive parts, jigs, fixtures, Industrial parts, and prototyping, PET-GF15 offers excellent toughness and resists brittleness. Whether you’re a professional engineer or advanced hobbyist, PET-GF15 delivers industrial-grade results with a user-friendly experience.

Fiberon PET-GF15 Technical Specifications

Nozzle Temperature 280 - 310 °C
Build Plate Temperature Room temp. - 60 °C
Cooling Fan ON
Printing Speed Up to 250 mm/s
Nozzle Type Hardened nozzle required
Drying Temperature and Time 70 °C / 8H
Annealing Temperature and Time 120 °C / 16H
Density 1.43 g/cm³ at 23 °C
Melt Index 36.9 g/10min (270°C, 2.16 kg)
Flame Retardancy HB (UL 94, 1.5mm)
Surface Resistivity (Ω) OL, >10¹² Ω (ANSI ESD S11.11)
Glass Transition Temperature 59.5 °C
Melting Temperature 231.6 °C
Crystallization Temperature 201.4 °C
Decomposition Temperature 422.8 °C
Vicat Softening Temperature 232.6 °C
Heat Deflection Temp. (1.8 MPa) — Annealed 87.3 °C
Heat Deflection Temp. (0.45 MPa) — Annealed 133.7 °C
Heat Deflection Temp. (1.8 MPa) — As Printed 71.8 °C
Heat Deflection Temp. (0.45 MPa) — As Printed 81.6 °C
Young's Modulus (X-Y) 4144.2 ± 133.3 MPa
Young's Modulus (Z) 3428.9 ± 257.2 MPa
Tensile Strength (X-Y) 59.9 ± 0.8 MPa
Tensile Strength (Z) 48.2 ± 0.3 MPa
Elongation at Break (X-Y) 4.0 ± 0.5%
Elongation at Break (Z) 2.6 ± 0.1%
Bending Modulus (X-Y) 3705.4 ± 84.5 MPa
Bending Modulus (Z) 2998.4 ± 92.3 MPa
Bending Strength (X-Y) 104.2 ± 2.4 MPa
Bending Strength (Z) 80.3 ± 2.5 MPa
Charpy Impact Strength (X-Y) Notched 8.7 ± 0.6 kJ/m²
Charpy Impact Strength (X-Y) Un-notched 27.2 ± 2.0 kJ/m²
Charpy Impact Strength (Z) Un-notched 13.9 ± 1.6 kJ/m²