Home PolyLite PLA Sparkle

PolyLite PLA Sparkle

Selected:
Size: 1.75MM | Weight: 1KG | Color: Sparkle Dark Green
Sale price AED 100.00
Size: 1.75MM
Weight: 1KG
Color: Sparkle Dark Green
SKU: PA02027
Features:
  • Eye-Catching Sparkle Finish
  • Jam-Free™ Technology
  • Exceptional Rigidity and Strength
Add to Wishlist Add to Compare

Notify me when available

Register to receive a notification when this item comes back in stock.

Compare color

PolyLite PLA Sparkle
Sparkle Dark Green
PolyLite PLA Sparkle
Sparkle Dark Blue

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
Striking Shimmering Finish and Deep Cosmic Aesthetic
PolyLite™ PLA Sparkle is a premium filament infused with distinct glitter particles, designed to give your 3D prints a futuristic and eye-catching aesthetic. It suspends highly reflective glitter within a rich matrix to deliver a stunning, starry-night visual effect for your projects.
Enhanced Heat Resistance and Excellent Dimensional Accuracy
Formulated with Polymaker's proprietary Jam-Free™ technology, this filament offers increased heat stability to prevent premature melting and ensure smooth, consistent extrusion. Built upon a high-quality Natureworks PLA base, it offers low shrinkage and excellent rigidity so your printed parts maintain reliable mechanical strength and tight tolerances.
Flawless Surface Quality and Ideal for Sci-Fi and Automotive Prints
Choose PolyLite™ PLA Sparkle for creating standout display pieces and highly visual decorative items, utilizing a wear-resistant nozzle to maintain optimal print quality.
Perfect for creating aerospace models, sci-fi props, and visually dynamic prototypes, especially when paired with a hardened steel nozzle to handle the abrasive glitter additives.

PolyLite PLA Sparkle Technical Specifications

Nozzle Temperature 190 - 220 °C
Build Surface Material BuildTak®, Glass, Blue Tape
Build Surface Treatment None
Build Plate Temperature 40 - 55 °C
Cooling Fan Turned On
Printing Speed 60 mm/s
Raft Separation Distance 0.2 mm
Retraction Distance 1 mm
Retraction Speed 20 mm/s
Recommended Environmental Temperature Room temperature - 45 °C
Threshold Overhang Angle 45°
Recommended Support Material PolySupport™
Density 1.17 - 1.24 g/cm³ at 21.5 °C
Glass Transition Temperature 61 °C
Vicat Softening Temperature 63 °C
Melt Index 7 - 11 g/10min (210°C, 2.16 kg)
Melting Temperature 150 °C
Crystallization Temperature 114 °C
Young's Modulus (X-Y) 2636 ± 330 MPa
Tensile Strength (X-Y) 46.6 ± 0.9 MPa
Tensile Strength (Z) 43.5 ± 3.1 MPa
Elongation at Break (X-Y) 1.9 ± 0.2%
Bending Modulus 3283 ± 132 MPa
Bending Strength 85.1 ± 2.9 MPa
Charpy Impact Strength 2.7 ± 0.2 kJ/m²