Home PolyLite PC

PolyLite PC

Selected:
Size: 1.75MM | Weight: 1 KG | Color: Transparent
Polymaker

Selling fast! 8 people have this in their carts.

Sale price AED 130.00
Size: 1.75MM
Weight: 1 KG
Color: Transparent
SKU: PC01001
Features:
  • Engineered Polycarbonate for 3D Printing
  • Light Diffusing and Translucent Properties
  • Simple Printing with Enclosure
Add to Wishlist Add to Compare
Order in the next to get it between and

Ask a question
Share

Return within 2 days of purchase.

Guarantee Safe Checkout

Visa
Mastercard
American Express
Diners Club
Apple Pay
Google Pay
Tabby
PolyLite PC

PolyLite PC
Engineered Polycarbonate for 3D Printing
PolyLite™ PC is crafted from a polycarbonate resin specifically designed for 3D printing, ensuring reliable performance and ease of use. This formulation provides excellent stiffness and heat resistance, making it suitable for demanding applications.
Light Diffusing and Translucent Properties
With its impressive translucency, PolyLite™ PC allows light to pass through, making it an excellent choice for projects that require light diffusion or aesthetic illumination effects.
Simple Printing with Enclosure
For best results, print PolyLite™ PC in an enclosure that traps ambient air. This helps maintain stable temperatures and produces stunning, high-quality prints with minimal warping.
Ideal for Functional and Aesthetic Parts
Choose PolyLite™ PC when you need a filament that combines stiffness, heat resistance, and beautiful translucency - perfect for both functional components and visually striking models.

PolyLite PC Technical Specifications

Nozzle Temperature 250 - 270 °C
Build Surface Treatment Texture PEI (Glue when needed)
Build Plate Temperature 90 - 105 °C
Cooling Fan OFF
Printing Speed 50 - 200 mm/s
Retraction Distance 1 - 3 mm
Retraction Speed 20 - 40 mm/s
Closure Chamber Needed (70 - 100 °C)
Recommended Support Material -
Drying Setting 75 °C / 6H
Annealing Setting 90 °C / 2H
Density 1.19 g/cm³ at 23 °C
Melt Index 8 - 11 g/10min (260°C, 2.16 kg)
Light Transmission 89% (GB/T 2410)
Flame Retardancy N/A
Glass Transition Temperature 113 °C
Melting Temperature N/A
Crystallization Temperature N/A
Decomposition Temperature > 360 °C
Vicat Softening Temperature 120 °C
Heat Deflection Temperature (1.8 MPa) 107 °C
Heat Deflection Temperature (0.45 MPa) 111 °C
Young's Modulus (X-Y) 2497 ± 154 MPa
Young's Modulus (Z) 2371 ± 55 MPa
Tensile Strength (X-Y) 69.1 ± 3.0 MPa
Tensile Strength (Z) 52.8 ± 1.7 MPa
Elongation at Break (X-Y) 4.8 ± 0.9%
Elongation at Break (Z) 2.7 ± 0.1%
Bending Modulus (X-Y) 2640 ± 47 MPa
Bending Modulus (Z) N/A
Bending Strength (X-Y) 106.1 ± 1.6 MPa
Bending Strength (Z) N/A
Charpy Impact Strength (X-Y) Notched 4.1 ± 0.9 kJ/m²
Charpy Impact Strength (Z) Notched N/A